Metallic mirror, metallic rotary polygonal mirror, and process for their production

ABSTRACT

A metallic mirror comprising a substrate made of aluminum or an aluminum alloy, and superposingly provided thereon in order an intermediate layer formed of TiO 2  and a metallic reflective layer formed of Cu. The metallic mirror may be a metallic mirror which further comprises a protective layer including at least a layer of Al 2 O 3 , formed by vacuum deposition on the metallic reflective layer. Also disclosed is a process for producing a metallic mirror, comprising the steps of forming the intermediate layer by vacuum deposition on a metallic polygonal mirror substrate metal, forming the metallic reflective layer of Cu by vacuum deposition on the intermediate layer, and forming the protective layer by vacuum deposition on the metallic reflective layer.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] This invention relates to a metallic mirror and a metallic rotary polygonal mirror which are usable as reflecting mirrors in copying machines, facsimile machines, laser beam printers or the like and as mirrors for mircrochip optical scanners, and also relates to a process for their production. More particularly, this invention relates to a metallic mirror and a metallic rotary polygonal mirror which have a superior environmental stability and a stability in reflectance, having a high reflectance, and a process for their production.

[0003] 2. Related Background Art

[0004] Conventionally available metallic rotary polygonal mirrors include, e.g., the following (1), (2) and (3).

[0005] (1) A metallic mirror whose rotary polygonal mirror substrate made of aluminum or an aluminum alloy has been anodized on its cut mirror surface to form a transparent film (anodic oxide film) to provide a mirror-surface protective film (Japanese Patent Application Laid-Open No. 58-184903).

[0006] (2) A metallic mirror whose rotary polygonal mirror substrate made of aluminum or an aluminum alloy is provided with a metallic thin film of Cr formed by vacuum deposition and further provided thereon with a high-reflectance metallic thin film of Cu formed by vacuum deposition (Japanese Patent Application Laid-Open No. 60-195502).

[0007] (3) A metallic mirror whose rotary polygonal mirror substrate made of aluminum or an aluminum alloy is provided with an intermediate layer, a metallic reflective layer and a protective film which are formed by vacuum deposition in order; the intermediate layer being a Cr layer having a layer thickness of from 50 nm to 100 nm, the metallic reflective layer a Cu layer having a layer thickness of from 100 nm to 150 nm, and the protective film an Al₂O₃ layer having a layer thickness of from 150 nm to 200 nm (Japanese Patent Application Laid-Open No. 6-208076).

[0008] Of the above conventional metallic mirrors, the mirror (1) has an average reflectance of about 85%, which can not be said to be a sufficient reflectance for the achievement of higher speed in copying machines and laser beam printers. Also, when the anodic oxide film is formed on the substrate made of aluminum or an aluminum alloy, the presence of any impurities such as Si on the rotary polygonal mirror substrate may possibly cause pit-like defects in the anodic oxide film. Accordingly, the aluminum or aluminum alloy must be those having a high purity, and hence expensive materials are required for the rotary polygonal mirror substrate, resulting in a high cost.

[0009] As for the mirrors (2) and (3), they have a high reflectance, but have a problem on environmental stability. When these metallic rotary polygonal mirrors are placed in a high-temperature and high-humidity environment (e.g., 45° C., 95%RH, 100 hrs, O₃ 1 ppm; or 70° C., 85%RH, 100 hrs, O₃ 1 ppm), the following phenomena may take place.

[0010] i) As shown diagrammatically in FIG. 3, dissolution reaction of metal and reduction reaction of oxygen take place, which are considered due to formation of local cells. What makes this reaction takes place is water-absorptive dust adhered to the film surface, where H₂O enters the film locally. Oxygen dissolved in the water is further involved, and the water passes from the outermost layer through SiO₂→Al₂O₃→Cu→Cr to reach the underlying substrate Al. As the result, an oxide of Al is formed to come into Al₂O₃, which causes volume expansion to raise the film lit, resulting in defects. This phenomenon can be explained by oxidation reduction reaction as shown by the following scheme.

[0011] Anode: Al→Al³+3_(e-) (dissolution reaction of Al)

[0012] Cathode: O₂+2H₂O+4_(e-)→40H— (reduction reaction of oxygen)

[0013] Optical-microscope photographs and a cross-sectional photograph [analysis by FIB (focused ion beam)] of such a corrosion phenomenon are shown in FIGS. 6 and 7 and FIG. 8, respectively.

[0014] More specifically, the present inventors placed in the high-temperature and high-humidity environment (45° C., 95%RH, 100 hrs, O₃ 1 ppm; or 70° C., 85%RH, 100 hrs, O₃ 1 ppm) a metallic rotary polygonal mirror comprised of an aluminum substrate, and a Cr layer as an intermediate layer, a Cu layer as a reflective layer and an Al₂O₃ layer (dielectric layer) and an SiO₂ layer as protective layers superposed on the aluminum substrate, and observed it. As a result, as shown in FIGS. 6 and 7 (both optical-microscope photographs at corroded portions) and FIG. 8 (an FIB cross-sectional photograph), corrosion was found to have occurred.

[0015] ii) A phenomenon of “film lifting” may occur as shown in a photograph 4 given as FIG. 9 and photographs 6 to 8 given as FIGS. 10 to 12. As can be seen from these cross-sectional photographs, films are separated at the interface between the intermediate layer Cr film and the reflective layer Cu film.

[0016] Measurement of each film stress between the intermediate layer Cr, the reflective layer Cu and the dielectric layer Al₂O₃ reveals that the Cr film has a stress of +4.15×10⁸ Pa, the Cu film +1.53×10⁸ Pa, and the Al₂O₃ film −0.63×10⁸ Pa, showing great differences in stress between them, which can be presumed to be caused by the separation between the Cr film and the Cu film.

SUMMARY OF THE INVENTION

[0017] Accordingly, an object of the present invention, which was made taking account of the problems the conventional techniques have had, is to provide a metallic mirror and a metallic rotary polygonal mirror which have a superior environmental resistance and a high reflectance, and a process for producing them.

[0018] Another object of the present invention is to provide a metallic mirror and a metallic rotary polygonal mirror which do not cause any phenomenon of film lifting, and a process for producing them.

[0019] The present invention provides a metallic mirror comprising a substrate made of aluminum or an aluminum alloy, and an intermediate layer of TiO₂ and a metallic reflective layer of Cu superposed on the substrate.

[0020] The present invention also provides a metallic mirror comprising a metallic polygonal mirror substrate made of aluminum or an aluminum alloy, an intermediate layer of TiO₂ formed by vacuum deposition on the substrate, a metallic reflective layer of Cu formed by vacuum deposition on the intermediate layer, and a protective layer which includes at least a layer of Al₂O₃ and is formed by vacuum deposition on the metallic reflective layer.

[0021] The present invention also provides a process for producing a metallic mirror, comprising the steps of;

[0022] forming an intermediate layer of TiO₂ by vacuum deposition on a metallic polygonal mirror substrate comprised of aluminum or an aluminum alloy;

[0023] forming a high-reflectance metallic reflective layer of Cu by vacuum deposition on the intermediate layer; and

[0024] forming a protective layer including at least a layer of Al₂O₃, by vacuum deposition on the metallic reflective layer.

[0025] It is considered that a good environmental stability attributable to the metallic mirror of the present invention can be explained in the following way.

[0026] A thin TiO₂ film formed as an intermediate layer between the mirror surface of rotary polygonal mirror substrate made of aluminum or an aluminum alloy and the metallic reflective layer Cu film can prevent H₂O and O₂ from entering through the film outermost layer in a high-humidity environment. As the result, the aluminum or aluminum alloy substrate can be kept from being oxidized into Al₂O₃ which brings about volume expansion to raise the film, so that corrosion damage is inhibited from occurring.

[0027] It is also considered that the advantage brought about by the metallic mirror of the present invention which do not cause any phenomenon of film lifting can be explained in the following way.

[0028] The stress of the various thin films of Cr (stress: +4.15×10⁸ Pa), Cu (stress: +1.53×10⁸ Pa) and Al₂O₃ (stress: −0.63×10⁸ Pa) has been greatly different between Cr and Cu films, whereas, in place of these, the thin films in the present invention are constituted of TiO₂ (stress: +0.30×10⁸ Pa), Cu and Al₂O₃, so that the difference in stress between the thin films can be minimized, and the phenomenon of “film lifting” can be prevented from occurring between the Cr and Cu films.

[0029] Here, the stress is measured by the Stoney's method in which stress is determined from warpage of each film formed as a single film on a glass substrate, and is calculated from the following equation.

Tress σ=EsD ²/[6(1−ν)R]

[0030] wherein:

[0031] Es: Young's modulus of the substrate;

[0032] D: thickness of the substrate;

[0033] ν: Poisson's ratio of the substrate; and

[0034] R: curvature of radius of warpage; and plus sign (+) indicates tensile direction, and minus sign (−) compression direction.

BRIEF DESCRIPTION OF THE DRAWINGS

[0035]FIG. 1 is a partial (about half) diagrammatic cross-sectional illustration of metallic rotary polygonal mirrors of Examples 1 and 2 according to the present invention.

[0036]FIG. 2 is a partial (about half) diagrammatic cross-sectional illustration of metallic rotary polygonal mirrors of Examples 3 and 4 according to the present invention.

[0037]FIG. 3 is a diagrammatic illustration of a phenomenon of corrosion.

[0038]FIG. 4 is a graph showing spectral characteristics of reflectance when TiO₂ [curved line (a)] or Cr₂O₃ [curved line (b)] is used as an intermediate-layer material.

[0039]FIG. 5 is a graph making a comparison between spectral characteristics of reflectance in S polarized light at an incident angle of 15° when a TiO₂ film is used as the intermediate layer [curved line (b): double-layer protective layer; curved line (c): triple-layer protective layer] and spectral characteristics of reflectance in S polarized light at incident angle of 15° when conventional Cr is used [curved line (a)].

[0040]FIG. 6 is an optical-microscope photograph showing corrosion of an intermediate layer in a conventional case.

[0041]FIG. 7 is an optical-microscope photograph showing corrosion of an intermediate layer in a conventional case.

[0042]FIG. 8 is an FIB cross-sectional photograph of a corroded portion.

[0043]FIG. 9 is an FIB cross-sectional photograph of a phenomenon of film lifting.

[0044]FIG. 10 is a surface optical-microscope photograph of the phenomenon of film lifting.

[0045]FIG. 11 is a surface optical-microscope photograph of the phenomenon of film lifting.

[0046]FIG. 12 is a surface optical-microscope photograph of the phenomenon of film lifting.

[0047]FIG. 13 is an SEM (scanning electron microscope) photograph of a Cr film surface.

[0048]FIG. 14 is an SEM (scanning electron microscope) photograph of a TiO₂ film surface.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0049] The metallic mirror of the present invention is usable as various types of mirrors such as a bathroom mirror, an automobile rearview mirror, a lamp reflecting mirror and a dentist's mirror. FIG. 1 shows an example in which the metallic mirror according to the present invention is used as a rotary polygonal mirror.

[0050] As shown in FIG. 1, on the periphery of a rotary polygonal mirror substrate 1 made of aluminum or an aluminum alloy, a mirror surface is formed by cutting or the like. Here is shown an example of an octahedral metallic rotary polygonal mirror, which, however, may be polygonal other than octahedral.

[0051] Such a mirror has an insufficient reflectance of about 86% in itself, and also the substrate can not be said to have a sufficient corrosion resistance. Accordingly, in the present invention, an intermediate layer formed of TiO₂ and a metallic reflective layer 3 formed of Cu are provided on this metallic polygonal mirror substrate 1. The Cu metallic reflective layer 3 has a higher reflectance than the substrate metal (i.e., aluminum or an aluminum alloy). This can make higher the reflectance required as a metallic rotary polygonal mirror. In the present invention, the TiO₂ intermediate layer 2 is provided so that the mirror surface of the substrate metal can be prevented from corrosion and the adhesion between the substrate and the high-reflectance metallic reflective layer can be improved.

[0052] In the present invention, the intermediate layer formed of TiO₂ may usually have a thickness of from 20 nm to 200 nm, preferably from 50 nm to 150 nm, and most preferably from 50 nm to 100 nm, because a too thin layer may have an insufficient durability and a too thick layer takes a long time for its formation, resulting in a poor productivity. In the present invention, the layer thickness refers to mechanical layer thickness unless otherwise specified.

[0053] The metallic reflective layer formed of Cu may also usually have a thickness of 80 nm or larger, preferably from 80 nm to 150 nm, and most preferably from 80 nm to 100 nm, because a too thin layer may have an insufficient reflectance and a too thick layer takes a long time for its formation, resulting in a poor productivity.

[0054] The TiO₂ intermediate layer and Cu metallic reflective layer may preferably be formed by, but not particularly limited to, deposition. This deposition includes vacuum deposition (in a narrow sense), sputtering and ion plating. With regard to the Cu film, it may be formed by a wet process such as plating, but in usual cases the deposition is preferred.

[0055] In the present invention, for the purpose of protecting the mirror surface and further for the purpose of also enhancing reflection, a protective layer which is comprised of one or more layers may preferably be provided on the surface of the metallic reflective layer. This protective layer is usually formed of a transparent dielectric material. In order to improve the function of protection or in order to enhance reflection more effectively, the protective layer may be of a multiple layer. In particular, it is preferred that a protective layer is alternately formed of, from the metallic reflective layer side, a dielectric material having a low refractive index and a dielectric material having a high refractive index because a high reflectance can be easily achieved.

[0056] The dielectric material having a low refractive index may include MgF₂, SiO₂ and Al₂O₃. As the dielectric material having a high refractive index, ZrO₂, TiO₂, CeO₂ and SiO are preferred. Also, in this case, each protective layer may preferably have a layer thickness which is so optimized as to maximize a reflectance at the desired wavelength and minimize dependence upon an angle of incident light.

[0057] The intermediate layer TiO₂ film is indispensable in order to improve the adhesion between the substrate metal and the high-reflectance metallic reflective layer thin film. This is the most important item in the present invention.

[0058] The present invention will be described below by giving Examples. FIG. 1 is a partial (about half) diagrammatic cross-sectional illustration of metallic rotary polygonal mirrors of Examples 1 and 2 according to the present invention. FIG. 2 is a partial (about half) diagrammatic cross-sectional illustration of metallic rotary polygonal mirrors of Examples 3 and 4 according to the present invention.

EXAMPLE 1

[0059] As shown in FIG. 1, on the metallic polygonal mirror substrate 1 made of an aluminum alloy (Al—Mg type), the intermediate layer 2, the metallic reflective layer 3, a protective layer (first protective layer) 4 and a protective layer (second protective layer) 5 were formed in order.

[0060] The intermediate layer 2 is a TiO₂ film, which may have a layer thickness of from 50 nm to 150 nm. If it has a thickness smaller than 50 nm, durability is insufficient. If it has a thickness larger than 150 nm, it takes a long time for deposition, resulting in a poor productivity.

[0061] When the intermediate layer comprised of this TiO₂ film is formed by vacuum deposition, the film may preferably be formed adding an O₂ gas under a pressure of from 6.65×10⁻³ Pa to 26.6×10⁻³ Pa (5×10⁻⁵ Torr to 2×10⁻⁴ Torr) as total pressure in the reaction space. If the O₂ gas pressure is lower than 6.65×10⁻³ Pa, it is considered that the underlying aluminum alloy have a poor affinity for the TiO₂ film, so that film separation tends to occur between the TiO₂ film and the Cu film. If on the other hand it is higher than 26.6×10⁻³ Pa, it is considered that the Cu film tends to be oxidized, so that the mirror may have a reflectance lower than the desired 95%. Accordingly, the O₂ added in order to prevent film separation while ensuring the desired reflectance of 95% or higher may preferably be at the pressure of from 6.65 to 26.6×10⁻³ Pa.

[0062] The metallic reflective layer 3 is a Cu film, which may have a layer thickness of from 80 nm to 150 nm. If the Cu film has a layer thickness smaller than 80 nm, a low reflectance may result. If it has a thickness larger than 150, it takes a long time for deposition, resulting in a poor productivity. The metallic reflective layer 3 is formed using a W (tungsten) boat resistance heating system as an evaporation material heating system.

[0063] When the high-reflectance metallic thin film of Cu is formed by vacuum deposition on the intermediate layer of TiO₂ film, it may preferably be formed after the inside of a vacuum deposition chamber reaches a degree of vacuum of 2.66×10⁻³ (2×10⁻⁵ Torr) Pa or above subsequently to the formation of the intermediate layer of TiO₂ film. If the inside of a vacuum deposition chamber has a degree of vacuum lower than 2.66×10⁻³ Pa, the mirror may have a reflectance lower than the desired 95%. On the other hand, a reflectance of the desired 95% or higher can be ensured when the Cu film is formed by vacuum deposition after the pressure has come to be 2.66×10⁻³ Pa or above. This is presumed as follows: Any excess gas components remaining in the vacuum deposition chamber can be made less when the chamber is brought into a high vacuum state before the deposition of Cu film, so that any residual gas can be prevented from entering the Cu film (to cause its oxidation), hence a Cu film with a high quality can be formed and the high reflectance can be ensured.

[0064] The protective layer (first protective layer) 4 is comprised of an Al₂O₃ film, and may have a layer thickness of from 150 nm to 200 nm. If the Al₂O₃ film has a layer thickness smaller than 150 nm, durability may be insufficient. If it has a layer thickness larger than 200 nm, the mirror may have insufficient optical characteristics such as reflecting properties inclusive of incident-angle dependence.

[0065] When the protective layer of Al₂O₃ is formed by vacuum deposition on the high-reflectance metallic thin film of Cu, the protective layer or film may preferably be formed by vacuum deposition i) without addition of any O₂ gas at the initial stage of film formation until the film comes to have a layer thickness of 15 to 30% of the stated layer thickness, in order to improve the affinity of the Al₂O₃ protective film for the Cu film, in other words, the former's adhesion to the latter, and ii) further thereon, after the film has been formed beyond 15 to 30% and until it comes to have the stated layer thickness, with addition of O₂ gas so that almost all the film has an Al:O ratio of 2:3, i.e., the film of Al₂O₃ sufficiently combined with oxygen. Even when the film is formed by vacuum deposition with addition of O₂ gas from beginning to end of the film formation, there is no problem in both reflectance and adhesion. The value of reflectance can be made higher by about 0.3 to 0.5% when as described above the film is formed by vacuum deposition without addition of any O₂ gas at the initial stage of film formation until the film comes to have a layer thickness of 15 to 30% of the stated layer thickness and further thereon with addition of O₂ gas after the film has been formed beyond 15 to 30% and until it comes to have the stated layer thickness.

[0066] This is presumed as follows: Where the O₂ gas is fed into the vacuum deposition chamber in order to form the protective layer of Al₂O₃ after the high-reflectance metallic thin film of Cu has been formed, the surface layer portion of the Cu film may undergo oxidation to result in a little low reflectance though the desired reflectance of 95% can be ensured, whereas the addition of no O₂ gas at the initial stage of film formation until the film comes to have a layer thickness of 15 to 30% of the stated layer thickness prevents the Cu film surface layer portion from being oxidized, so that the reflectance can be at a higher value. However, unless the O₂ gas is added after the film has been formed beyond 30%, though there is no problem on the reflectance, the film lifting may occur. Accordingly, the formation of the Al₂O₃ film without addition of any O₂ gas may be only at the initial stage of film formation during which the film comes to have a layer thickness of 15 to 30% of the stated layer thickness. Also, the amount of O₂ gas added when the Al₂O₃ film is deposited, i.e., the total pressure of reaction space that is substantially determined by the O₂ gas fed into the chamber may be within the range of from 6.65×10⁻³ Pa to 26.6×10⁻³ Pa taking account of any occurrence of film separation. The film of Al₂O₃ can be formed even without addition of O₂ gas when the Al₂O₃ film is formed. This is because oxygen atoms are contained in materials other than the O₂ gas and such materials are used in film formation.

[0067] The protective layer (second protective layer) 5 is an SiO₂ film, which may have a layer thickness of from 10 nm to 20 nm. If it has a layer thickness smaller than 10 nm, it may provide a low surface strength. If it has a layer thickness larger than 20 nm, the mirror may have insufficient optical characteristics such as reflecting properties.

[0068] Conditions for forming the respective films in Example 1 are shown in Table 1.

EXAMPLE 2

[0069] In Example 2, on the metallic polygonal mirror substrate 1 made of an aluminum alloy (Al—Mg type), an intermediate layer 2, a metallic reflective layer 3, a protective layer (first protective layer) 4 and a protective layer (second protective layer) 5 were formed in order. The intermediate layer 2, the metallic reflective layer 3, the protective layer (first protective layer) 4 and the protective layer (second protective layer) 5 were formed in the same manner as in Example 1 except that the metallic reflective layer 3 was formed by employing a deposition material heating system making use of electron beams.

[0070] Conditions for forming the respective films in Example 2 are shown in Table 2.

[0071] As can be seen from Tables 1 and 2, Examples 1 and 2 differ in the deposition material heating system for forming the metallic reflective layer. In Example 1, W (tungsten) boat resistance heating is used, but in Example 2 electron beams are used.

EXAMPLE 3

[0072] In Example 3, as shown in FIG. 2, on a metallic polygonal mirror substrate 1 made of an aluminum alloy (Al—Mg type), an intermediate layer 2, a metallic reflective layer 3, a protective layer (first protective layer) 4, a protective layer (second protective layer) 5 and a protective layer (third protective layer) 6 were formed in order. In Example 3, differently from Examples 1 and 2, a third protective layer is provided on the second protective layer. Also, in Example 3, the metallic reflective layer 3 was formed by employing W boat resistance heating as the deposition material heating system in the same manner as in Example 1. The intermediate layer 2, the metallic reflective layer 3 and the protective layer (first protective layer) 4 were also formed in the same manner, and details on these are omitted here accordingly.

[0073] The protective layer (second protective layer) 5 is comprised of a TiO₂ film, and may have a layer thickness of from 80 nm to 100 nm. If it has a layer thickness smaller than 80 nm or larger than 100 nm, the mirror may have insufficient optical characteristics such as reflecting properties inclusive of incident-angle dependence.

[0074] The protective layer (third protective layer) 6 is an SiO₂ film, which may have a layer thickness of from 10 nm to 20 nm. If it has a layer thickness smaller than 10 nm, it may provide a low surface strength. If it is in a thickness larger than 20 nm, the mirror may have insufficient optical characteristics such as reflecting properties.

[0075] Conditions for forming the respective films in Example 3 are shown in Table 3.

EXAMPLE 4

[0076] In Example 2, on the metallic polygonal mirror substrate 1 made of an aluminum alloy (Al—Mg type), an intermediate layer 2, a metallic reflective layer 3, a protective layer (first protective layer) 4, a protective layer (second protective layer) 5 and a protective layer (third protective layer) 6 were formed in order. The intermediate layer 2, the metallic reflective layer 3, the protective layer (first protective layer) 4, the protective layer (second protective layer) 5 and the protective layer (third protective layer) 6 were formed in the same manner as in Example 3 except that the metallic reflective layer 3 was formed by employing a deposition material heating system making use of electron beams.

[0077] Conditions for forming the respective films in Example 4 are shown in Table 4.

[0078] As can be seen from the accompanying Tables 3 and 4, Examples 3 and 4 differ in the deposition material heating system for forming the metallic reflective layer. In Example 3, W (tungsten) boat resistance heating is used, but in Example 4 electron beams are used.

[0079] With regard to the above Examples 1 to 4;

[0080] summarized in Table 5 is the relationship between i) the amount of O₂ gas added during deposition of the intermediate layer TiO₂, in other words, the total pressure of reaction space when the O₂ is added, ii) reflectance before and after a durability test (left standing under the conditions shown in the table) and iii) adhesion of the Cu film to the TiO₂ film;

[0081] in Table 6, the relationship between i) degree of vacuum during deposition of the metallic reflective layer Cu film and ii) reflectance before and after the durability test;

[0082] in Table 7, the relationship between i) layer thickness by which the O₂ gas is not added at the initial stage of deposition of the protective layer Al₂O₃ film, ii) reflectance before and after the durability test and iii) adhesion of the Al₂O₃ film to the Cu film; and

[0083] in Table 8, the relationship between i) the amount of O₂ gas added during deposition of the protective layer Al₂O₃ film, in other words, the total pressure of reaction space when the O₂ is added and ii) adhesion of the Al₂O₃ film to the Cu film.

[0084] In these tables, as to “A” and “C” shown as evaluation results in the item “adhesion”, “A” is a symbol indicating that film separation does not occur, and “C”, film separation occurs.

[0085] Also summarized in Table 9 are the results of evaluation on corrosion percentage after durability test, reflectance, film lifting percentage, adhesion, and wiping resistance.

[0086] As can be seen from Table 5, the film separation is seen to have occurred when the amount of O₂ gas added during deposition of the intermediate layer TiO₂, in other words, the total pressure of reaction space when the O₂ is added is below 6.65×10⁻³ Pa (0.5×10⁻⁴ Torr in Table 5). As also can be seen from Table 6, in the state the degree of vacuum during deposition of the Cu film is below 3.32×10⁻³ Pa (2.5×10⁻⁵ Torr), the reflectance is lower than 95% in some cases depending on wavelength. As still also can be seen from Table 7, the film separation is seen to have occurred when the layer thickness formed while the O₂ gas is not added from the beginning of deposition of the protective layer Al₂O₃ film is larger than 30% of the stated layer thickness (e.g., a layer thickness of 38%). As further can be seen from Table 8, the film separation is seen to have occurred when the amount of O₂ gas added during deposition of the protective layer Al₂O₃ film, in other words, the total pressure of reaction space is outside the range of from 6.65×10⁻³ Pa to 26.6×10⁻³ Pa. As still further can be seen from Table 9, both the adhesion and the wiping resistance are good in Examples 1 to 4.

[0087] To test the adhesion, a pressure-sensitive adhesive tape (available from Nichiban Co., Ltd.) was brought into close adhesion to the surface of the metallic rotary polygonal mirror, and then peeled therefrom at a rate of 20 mm/sec to visually examine whether or not the surface has peeled.

[0088] To test the wiping resistance, a sheet of lens cleaning paper (Dusper was used) was impregnated with a solvent (50 vol. % of ether+50 vol. % of methanol). This cleaning paper was pressed against the metallic rotary polygonal mirror at a pressure of 2 kg/cm2, and moved back and forth ten times, and thereafter, visual examination was made on whether or not any scratches are seen at the surface. In Table 9, “A” indicates that the surface was not scratched even by the wiping resistance test.

[0089] Comparative Test

[0090] As shown in Tables 10 and 11, films of various materials Cr, Ni, Ti, Ni—Cr (Cr: 20 wt. %), Cr₂O₃ (with O₂), Cr₂O₃ (without O₂), ZrO₂ (with O₂), Al₂O₃ (without O₂), SiO₂ (with O₂), Ta₂O₅ (without O₂) and TiO₂ (with O₂) were each formed by vacuum deposition in a layer thickness of 80 nm to 120 nm.

[0091] (“With O₂” shows that the film was deposited in an atmosphere with addition of O₂ at an O₂ partial pressure of 1.99×10⁻³ Pa.)

[0092] On each film thus formed, a thin film of Cu was superposed in a thickness of about 100 nm, and on the thin film of Cu an Al₂O₃ film was further formed in a thickness of 170 nm. Then as the outermost surface layer an SiO₂ film was formed in a thickness of 14 nm. The Al₂O₃ and SiO₂ films were formed at an O₂ partial pressure of 1.99×10⁻³ Pa.

[0093] Metallic rotary polygonal mirrors thus obtained were left standing in an atmosphere of 70° C., 85%RH and O₃ concentration of 1 ppm for 100 hours to examine their environmental properties. Layer configuration: Al/intermediate layer/Cu/Al₂O₃/SiO₂.

[0094] With regard to “Corrosion” in Table 10, even slight changes of mirror surface in appearance before and after the durability test were counted as the number of occurrence.

[0095] As the result, as shown in Tables 10 and 11, the following is seen.

[0096] (1) The adhesion of the metallic reflective layer to the substrate material satisfies the standard except for the sample having no intermediate layer.

[0097] (2) With regard to the corrosion, when examined by the method in which even slight changes of mirror surface in appearance before and after the durability test are counted as the number of occurrence, corrosion percentages are 10% or less in three types, Ni—Cr (Cr: 20 wt. %), Cr₂O₃ (with O₂) and TiO₂ (with O₂).

[0098] (3) When the reflectance at an incident angle 15° of S polarized light with wavelength of 655 nm, 675 nm and 780 nm each is examined before and after the durability test, almost all samples having the intermediate layers except for the TiO₂ film do not satisfy the standard of 95% or higher.

[0099] (4) With regard to the phenomenon of film lifting, oxide type intermediate layer materials are more effective for preventing its occurrence than metal type ones.

[0100] With regard to Cr₂O₃ (with O₂), showing good results on the above-(2) corrosion, the reflectance is not sufficient from the initial stage. FIG. 4 shows spectral characteristics of reflectance in respect of TiO₂ [curved line (a)] or Cr₂O₃ [curved line (b)]. As shown therein, the Cr₂O₃ results in an insufficient reflectance. With regard to Ni—Cr (Cr: 20 wt. %), showing good results on the above-(2) corrosion, there is a little problem on the phenomenon of film lifting and further there is another problem that the film formation speed is so low as to be not suitable for production.

[0101] In FIG. 5, spectral characteristics of reflectance in S polarized light at an incident angle of 15° are compared between when the TiO₂ film is used as the intermediate layer [curved line (b): double-layer protective layer; curved line (c): triple-layer protective layer) and when the conventional Cr is used [curved line (a)]. As can be seen therefrom, a reflectance comparable to or higher than conventional cases is obtainable also when the TiO₂ film is used as the intermediate layer.

[0102] To make sure that the TiO₂ film is superior as the intermediate layer, the state of film surface of each of the TiO₂ thin film and the Cr thin film was observed on an FESEM (field emission scanning electron microscope). The film surface of the Cr thin film is, as shown in FIG. 13, seen to have a columnar texture, and supposed to allow H₂O and O₂ to pass, whereas, as shown in FIG. 14, that of the TiO₂ thin film has a dense film structure, and is presumed to be able to prevent H₂O and O₂ from entering. TABLE 1 Substrate Degree of Deposition Deposition temperature vacuum rate Layers material heating (° C.) (Torr) (mm/sec) Intermediate Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 2 O₂ added Metallic W boat resistance 150 1.0 × 10⁻⁵ 2.0 refecting heating layer 3 Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 4 O₂ added* Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 5 O₂ added

[0103] TABLE 2 Substrate Degree of Deposition Deposition temperature vacuum rate Layers material heating (° C.) (Torr) (mm/sec) Intermediate Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 2 O₂ added Metallic Electron beams 150 1.0 × 10⁻⁵ 2.0 refecting layer 3 Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 4 O₂ added* Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 5 O₂ added

[0104] TABLE 3 Substrate Degree of Deposition Deposition temperature vacuum rate Layers material heating (° C.) (Torr) (mm/sec) Intermediate Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 2 O₂ added Metallic W boat resistance 150 1.0 × 10⁻⁵ 2.0 refecting heating layer 3 Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 4 O₂ added* Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 5 O₂ added Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 6 O₂ added

[0105] TABLE 4 Substrate Degree of Deposition Deposition temperature vacuum rate Layers material heating (° C.) (Torr) (mm/sec) Intermediate Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 2 O₂ added Metallic Electron beams 150 1.0 × 10⁻⁵ 2.0 refecting layer 3 Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 4 O₂ added* Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 5 O₂ added Protective Electron beams 150 1.5 × 10⁻⁴ 0.2 layer 6 O₂ added

[0106] TABLE 5 Amount of O₂ gas added Reflectance (S polarized light) during deposition of Before durability test After durability test intermediate layer TiO₂ 655 nm 675 nm 780 nm 655 nm 675 nm 780 nm Adhe- (×10⁻⁴ Torr) (%) (%) (%) (%) (%) (%) sion 0.0 Example 1: 96.2 96.3 97.2 96.1 96.3 97.2 C Example 2: 95.3 95.9 96.9 95.2 95.8 96.8 C Example 3: 97.2 97.6 98.0 97.0 97.2 97.6 C Example 4: 97.1 97.7 98.0 96.9 97.4 97.8 C 0.3 Example 1: 96.3 96.7 97.5 96.1 96.5 97.3 C Example 2: 95.5 96.0 97.0 95.3 96.0 96.9 C Example 3: 97.2 97.5 98.1 97.0 97.4 97.8 C Example 4: 97.4 97.9 98.4 97.1 97.8 98.2 C 0.5 Example 1: 96.4 96.7 97.5 96.2 96.5 97.4 A Example 2: 95.4 96.0 97.1 95.2 95.8 97.0 A Example 3: 97.3 97.7 98.4 97.1 97.6 98.3 A Example 4: 97.4 98.0 98.5 97.2 97.8 98.3 A 1.0 Example 1: 96.6 96.7 97.6 96.5 96.7 97.7 A Example 2: 95.6 96.1 97.2 95.4 96.0 97.1 A Example 3: 97.4 97.8 98.5 97.2 97.6 98.3 A Example 4: 97.5 98.0 98.7 97.3 97.8 98.7 A 1.2 Example 1: 96.3 96.8 97.6 96.1 96.7 97.4 A Example 2: 95.5 96.0 97.0 95.3 96.3 97.7 A Example 3: 97.5 97.9 98.5 97.4 97.8 98.4 A Example 4: 97.6 98.0 98.7 97.4 97.9 98.6 A 1.5 Example 1: 96.1 96.3 97.2 96.0 96.3 97.2 A Example 2: 95.5 96.1 97.1 95.4 96.3 97.7 A Example 3: 97.5 98.0 98.6 97.3 97.8 98.5 A Example 4: 97.7 98.2 98.8 97.5 98.1 98.7 A 2.0 Example 1: 95.5 96.0 97.0 95.3 95.7 96.7 A Example 2: 95.4 95.8 96.8 95.2 95.6 96.6 A Example 3: 95.9 97.6 98.4 95.7 97.4 98.2 A Example 4: 96.7 97.9 98.2 96.5 97.7 98.0 A 2.5 Example 1: 94.4 95.3 96.7 93.9 94.9 95.8 A Example 2: 94.2 95.2 96.4 93.7 94.6 95.9 A Example 3: 95.0 96.8 97.5 94.8 96.1 96.9 A Example 4: 95.0 96.7 97.4 94.7 96.4 96.9 A

[0107] TABLE 6 Degree of vacuum Reflectance (S polarized light) during deposition Before durability test After durability test of Cu 655 nm 675 nm 780 nm 655 nm 675 nm 780 nm (×10⁻⁵ Torr) (%) (%) (%) (%) (%) (%) 0.5 Example 1: 96.4 96.6 97.5 96.3 96.5 97.4 Example 2: 95.9 96.2 97.1 95.8 96.1 97.0 Example 3: 97.6 98.2 98.6 97.5 98.1 98.5 Example 4: 97.6 98.0 98.8 97.3 97.9 98.5 0.8 Example 1: 96.3 96.5 97.5 96.2 96.4 97.4 Example 2: 95.9 96.3 97.2 95.8 96.2 97.1 Example 3: 97.5 98.1 98.7 97.4 98.0 98.6 Example 4: 97.7 98.1 98.8 97.5 98.0 98.6 1.0 Example 1: 96.1 96.3 97.2 96.0 96.3 97.2 Example 2: 95.5 96.1 97.1 95.4 96.3 97.7 Example 3: 97.5 98.0 98.6 97.3 97.8 98.5 Example 4: 97.7 98.2 98.8 97.5 98.1 98.7 1.5 Example 1: 96.0 96.2 97.0 95.8 96.0 96.9 Example 2: 95.5 96.0 97.2 95.4 96.2 97.1 Example 3: 97.4 98.0 98.5 97.3 97.9 98.4 Example 4: 97.6 98.2 98.7 97.5 98.0 98.5 2.0 Example 1: 95.8 96.0 96.8 95.7 96.0 96.6 Example 2: 95.3 95.9 97.0 95.2 95.7 96.8 Example 3: 97.2 97.9 98.3 97.0 97.7 98.1 Example 4: 97.3 98.0 98.6 97.0 97.8 98.3 2.5 Example 1: 95.2 95.9 96.5 94.8 95.6 96.4 Example 2: 95.0 95.8 96.8 94.8 95.5 96.6 Example 3: 95.7 96.6 97.5 94.9 95.9 97.2 Example 4: 95.7 96.7 97.6 94.9 95.8 97.3 3.0 Example 1: 94.9 95.7 96.0 94.4 95.4 95.7 Example 2: 94.7 95.5 96.5 94.2 95.2 95.8 Example 3: 95.4 96.5 96.9 94.9 96.2 96.5 Example 4: 95.5 96.4 97.5 94.8 95.9 96.8

[0108] TABLE 7 Reflectance (S polarized light) Layer thickness by which Before durability test After durability test no O₂ gas wa added after 655 nm 675 nm 780 nm 655 nm 675 nm 780 nm Adhe- start of Al₂O₃ (%) (%) (%) (%) (%) (%) sion O₂ gas added Example 1: 96.1 96.3 97.2 96.0 96.3 97.2 A throughout Example 2: 95.5 96.1 97.1 95.4 96.3 97.7 A deposition Example 3: 97.5 98.0 98.6 97.3 97.8 98.5 A Example 4: 97.7 98.2 98.8 97.5 98.1 98.7 A 8% of the stated Example 1: 96.0 96.3 97.2 96.0 96.2 97.1 A layer thickness Example 2: 95.5 96.1 97.1 95.3 96.0 97.0 A Example 3: 97.5 98.0 98.5 97.4 97.8 98.4 A Example 4: 97.7 98.2 98.8 97.5 98.1 98.7 A 15% of the stated Example 1: 96.5 96.7 97.7 96.4 96.7 97.7 A layer thickness Example 2: 95.8 96.4 97.4 95.7 96.3 97.3 A Example 3: 97.8 98.2 98.6 97.7 98.2 98.5 A Example 4: 97.8 98.4 98.8 97.7 98.3 98.7 A 23% of the stated Example 1: 96.6 96.7 97.7 96.4 96.5 97.6 A layer thickness Example 2: 95.9 96.5 97.5 95.8 96.4 97.4 A Example 3: 97.9 98.2 98.7 97.8 98.1 98.6 A Example 4: 97.8 98.4 98.9 97.7 98.3 98.7 A 30% of the stated Example 1: 96.6 96.8 97.8 96.5 96.4 97.7 A layer thickness Example 2: 95.9 96.4 97.4 95.7 96.3 97.4 A Example 3: 97.8 98.2 98.6 97.7 98.1 98.5 A Example 4: 97.9 98.5 98.9 97.8 98.4 98.8 A 38% of the stated Example 1: 96.3 96.6 97.5 96.2 96.4 97.4 C layer thickness Example 2: 95.6 96.2 97.0 95.4 96.0 96.9 C Example 3: 97.6 98.0 98.4 97.5 97.9 98.3 C Example 4: 97.7 98.1 98.7 97.6 98.0 98.5 C 46% of the stated Example 1: 96.3 96.5 97.5 96.2 96.4 97.4 C layer thickness Example 2: 95.6 96.1 97.0 95.5 96.0 96.9 C Example 3: 97.5 98.0 98.5 97.4 97.9 98.4 C Example 4: 97.6 98.0 98.7 97.5 97.9 98.6 C 54% of the stated Example 1: 96.2 96.4 97.2 96.0 96.2 97.0 C layer thickness Example 2: 95.5 96.0 96.9 95.4 96.0 96.9 C Example 3: 97.4 97.9 98.5 97.3 97.8 98.4 C Example 4: 97.5 97.9 98.6 97.4 97.8 98.5 C 62% of the stated Example 1: 96.1 96.3 97.1 96.0 96.2 97.1 C layer thickness Example 2: 95.4 95.9 96.8 95.2 95.6 96.5 C Example 3: 97.3 97.7 98.4 97.1 97.5 98.2 C Example 4: 97.4 97.8 98.5 97.3 97.7 98.4 C

[0109] TABLE 8 Amount of O₂ gas added during deposition of Al₂ O₃ (×10⁻⁴ Torr) Adhesion 0.0 Example 1 C Example 2 C Example 3 C Example 4 C 0.3 Example 1 C Example 2 C Example 3 C Example 4 C 0.5 Example 1 A Example 2 A Example 3 A Example 4 A 1.0 Example 1 A Example 2 A Example 3 A Example 4 A 1.2 Example 1 A Example 2 A Example 3 A Example 4 A 1.5 Example 1 A Example 2 A Example 3 A Example 4 A 2.0 Example 1 A Example 2 A Example 3 A Example 4 A 2.2 Example 1 C Example 2 C Example 3 C Example 4 C 2.5 Example 1 C Example 2 C Example 3 C Example 4 C

[0110] TABLE 9 Film Reflectance (S polarized light) Corrosion lifting Before durability test After durability test Wiping percentage percentage 655 nm 675 nm 780 nm 655 nm 675 nm 780 nm Adhe- resist- (%) (%) (%) (%) (%) (%) (%) (%) sion ance Example: 1 5.2 0.0 96.1 96.3 97.2 96.0 96.3 97.2 A A 2 3.3 0.0 95.5 96.1 97.1 95.4 96.3 97.7 A A 3 3.7 0.0 97.5 98.0 98.6 97.3 97.8 98.5 A A 4 4.0 0.0 97.7 98.2 98.8 97.5 98.1 98.7 A A

[0111] TABLE 10 Corrosion Number of Per- Reflectance (S polarized light) occurence/ cent- Before durability test After durability test Intermediate layer number age 655 nm 675 nm 780 nm 655 nm 675 nm 780 nm Adhe- material of exam. (%) (%) (%) (%) (%) (%) (%) sion Cr 125/190 65.8 96.5 96.5 97.2 97.0 97.1 97.0 A None 13/20 65.0 94.7 95.6 96.7 93.0 94.3 96.6 C Ni 12/20 60.0 88.4 90.9 95.4 84.3 87.3 92.7 A Ti 10/20 50.0 95.4 95.7 96.7 93.2 94.2 96.5 A Ni-Cr(20)  2/20 10.0 96.2 96.5 97.2 96.3 96.5 97.1 A Cr₂O₃ (with O₂)  3/60  5.0 85.8 89.1 94.5 82.2 86.6 93.7 A Cr₂O₃ (without O₂) 12/60 20.0 94.6 95.9 96.8 94.3 95.4 96.9 A ZrO₂ (with O₂)  7/60 11.7 91.1 94.0 96.3 90.4 92.7 96.7 A Al₂O₃ (without O₂)  4/20 20.0 94.7 95.6 96.6 94.0 94.7 96.8 A SiO₂ (with O₂)  7/20 35.0 91.7 93.3 96.0 91.0 93.0 96.4 A Ta₂O₅ (with O₂)  8/20 40.0 94.3 95.5 97.0 95.3 96.5 97.0 A Ta₂O₅ (without O₂) 11/60 18.3 94.5 95.7 96.9 95.3 96.1 97.0 A TiO₂ (with O₂)  6/180  3.3 95.5 96.1 97.1 95.4 96.3 97.7 A

[0112] TABLE 11 Phenomenon of film lifting Intermediate Number of occurrence/ Percentage Wiping layer material number of examination (%) resistance test Cr 45/190 23.7 A None 9/20 45.0 A Ni 8/20 40.0 A Ti 7/20 35.0 A Ni—Cr (20) 6/20 30.0 A Cr₂O₃ (with O₂) 0/60 0.0 A Cr₂O₃ (without O₂) 0/60 0.0 A ZrO₂ (with O₂) 3/60 5.0 A Al₂O₃ (without O₂) 1/20 5.0 A SiO₂ (with O₂) 2/20 10.0 A Ta₂O₅ (with O₂) 0/20 0.0 A Ta₂O₅ (without O₂) 2/60 3.3 A TiO₂ (with O₂)  0/180 0.0 A 

What is claimed is:
 1. A metallic mirror comprising a substrate made of aluminum or an aluminum alloy, and an intermediate layer formed of TiO₂ and a metallic reflective layer formed of Cu which are superposed on the substrate in order.
 2. The metallic mirror according to claim 1 , which further comprises one or more protective layers provided on said metallic reflective layer.
 3. The metallic mirror according to claim 1 , which has a surface reflectance of 95% or higher.
 4. The metallic mirror according to claim 1 , which is a metallic rotary polygonal mirror.
 5. The metallic mirror according to claim 2 , wherein said protective layer is an aluminum oxide layer.
 6. A metallic rotary polygonal mirror comprising; a metallic polygonal mirror substrate made of aluminum or an aluminum alloy; an intermediate layer of TiO₂ formed by vacuum deposition on the substrate; a metallic reflective layer of Cu formed by vacuum deposition on the intermediate layer; and a protective layer including at least a layer of Al₂O₃, formed by vacuum deposition on the metallic reflective layer.
 7. The metallic rotary polygonal mirror according to claim 6 , wherein; said intermediate layer has a layer thickness of from 50 nm to 150 nm, and said metallic reflective layer has a layer thickness of from 80 nm to 150 nm.
 8. The metallic rotary polygonal mirror according to claim 6 , wherein; said protective layer comprises a double layer consisting of a first protective layer and a second protective layer.
 9. The metallic rotary polygonal mirror according to claim 8 , wherein; said first protective layer is a layer of Al₂O₃, and said second protective layer is a layer of SiO₂.
 10. The metallic rotary polygonal mirror according to claim 9 , wherein; said first protective layer has a layer thickness of from 150 nm to 200 nm, and said second protective layer has a layer thickness of from 10 nm to 20 nm.
 11. The metallic rotary polygonal mirror according to claim 6 , wherein; said protective layer comprises a triple layer consisting of a first protective layer, a second protective layer and a third protective layer.
 12. The metallic rotary polygonal mirror according to claim 11 , wherein; said first protective layer is a layer of Al₂O₃, said second protective layer is a layer of TiO₂, and said third protective layer is a layer of SiO₂.
 13. The metallic rotary polygonal mirror according to claim 12 , wherein; said first protective layer has a layer thickness of from 150 nm to 200 nm, said second protective layer has a layer thickness of from 80 nm to 100 nm, and said third protective layer has a layer thickness of from 10 nm to 20 nm.
 14. The metallic rotary polygonal mirror according to claim 6 , which has a surface reflectance of 95% or higher.
 15. A process for producing a metallic rotary polygonal mirror, comprising the steps of; forming an intermediate layer of TiO₂ by vacuum deposition on a metallic polygonal mirror substrate metal comprised of aluminum or an aluminum alloy; forming a high-reflectance metallic reflective layer of Cu by vacuum deposition on the intermediate layer; and forming a protective layer including at least a layer of Al₂O₃, by vacuum deposition on the metallic reflective layer.
 16. The process for producing a metallic rotary polygonal mirror according to claim 15 , wherein; during the formation of said intermediate layer of TiO₂, O₂ gas is added under a pressure of from 6.65×10⁻³ Pa to 26.6×10⁻³ Pa.
 17. The process for producing a metallic rotary polygonal mirror according to claim 15 , wherein; during the formation of said high-reflectance metallic reflective layer of Cu, the metallic reflective layer is formed after the inside of a vacuum deposition chamber reaches a degree of vacuum of 2.66×10⁻³ Pa or above subsequently to the formation of said intermediate layer of TiO₂ film.
 18. The process for producing a metallic rotary polygonal mirror according to claim 15 , wherein; in the formation of said protective layer including at least a layer of Al₂O₃, when the layer of Al₂O₃ is formed on said high-reflectance metallic thin film of Cu, the protective layer is formed without addition of any O₂ gas at the initial stage of film formation until the film comes to have a layer thickness of 15 to 30% of a stated layer thickness, and further thereon, after the film has been formed beyond 15 to 30% and until it comes to have the stated layer thickness, with addition of O₂ gas under a pressure of from 6.65×10⁻³ Pa to 26.6×10⁻³ Pa.
 19. The process for producing a metallic rotary polygonal mirror according to claim 15 , wherein; said intermediate layer is formed in a layer thickness of from 50 nm to 150 nm, and said metallic reflective layer is formed in a layer thickness of from 80 nm to 150 nm.
 20. The process for producing a metallic rotary polygonal mirror according to claim 15 , wherein; said protective layer is formed in a double layer consisting of a first protective layer and a second protective layer.
 21. The process for producing a metallic rotary polygonal mirror according to claim 20 , wherein; said first protective layer is a layer of Al₂O₃, and said second protective layer is a layer of SiO₂.
 22. The process for producing a metallic rotary polygonal mirror according to claim 21 , wherein; said first protective layer is formed in a layer thickness of from 150 nm to 200 nm, and said second protective layer is formed in a layer thickness of from 10 nm to 20 nm.
 23. The process for producing a metallic rotary polygonal mirror according to claim 15 , wherein; said protective layer is formed in a triple layer consisting of a first protective layer, a second protective layer and a third protective layer.
 24. The process for producing a metallic rotary polygonal mirror according to claim 23 , wherein; said first protective layer is a layer of Al₂O₃, said second protective layer is a layer of TiO₂, and said third protective layer is a layer of SiO₂.
 25. The process for producing a metallic rotary polygonal mirror according to claim 24 , wherein; said first protective layer is formed in a layer thickness of from 150 nm to 200 nm, said second protective layer is formed in a layer thickness of from 80 nm to 100 nm, and said third protective layer is formed in a layer thickness of from 10 nm to 20 nm.
 26. The process for producing a metallic rotary polygonal mirror according to claim 15 , wherein; said metallic rotary polygonal mirror has a surface reflectance of 95% or higher. 